Hardox® wear-resistant plate is worldwide well known wear-resistant material. Hardox® is perfectly hard steel – from the surface to the core. The result is a longer service life of parts even in the most demanding environments.
Hardox® 400 is wear-resistant steel with a nominal hardness of 400 HBW. The steel has high toughness (45J/-40°C), good bendability and weldability. It can be machined and drilled even without the use of special tools.
Hardox 400 is available as standard in the following variants:
- thickness 3 – 8 mm; sheet size 1500×3000 mm
- thickness 4 – 130 mm; sheet size 2000×6000 mm
The most widely used wear-resistant steel with excellent structural properties.Hardox® 450 is wear-resistant steel with a nominal hardness of 450 HBW. Hardox® 450 has toughness (50J/-40°C), offers good bendability and weldability.
Hardox 450 is available as standard in the following variants:
- thickness 2 – 8 mm; sheet size 1500 x 3000 mm
- thickness 4 – 130 mm; sheet size 2000 x 6000 mm
- thickness 4 – 50 mm; sheet size 2500 x 6000 mm
Hardox® 500 is a weldable and bendable steel with high abrasion resistance with a nominal hardness of 500 HBW. At the same time, this material is characterized by good toughness and weldability.
Hardox 500 is available as standard in the following variants:
- thickness 3 – 7 mm; sheet size 1500 x 3000 mm
- thickness 6 – 100 mm; sheet size 2000 x 4000 mm
- thickness 6 – 70 mm; sheet size 2000 x 6000 mm
Hardox 500 Tuf steel combines the best properties of Hardox® 450 and Hardox® 500 steels. The nominal hardness is 490 HBW.
Hardox 500 Tuf is available as standard in the following variants:
- thickness 4 – 25.4 mm; sheet size 2500 x 6000 mm
Hardox® 600 is a wear-resistant steel with a nominal hardness of 600 HBW and exceptionally high impact strength.
Material suitable for highly stressed parts (knives, armor…). Can be cut and welded, very difficult machining.
Hardox 600 is available as standard in the following variants:
- thickness 5 – 60 mm; sheet size 2000 x 4000 (6000) mm
The hardest HARDOX sheet with a hardness of up to 700 HBW. It is designed for extremely stressed parts. Can be processed by burning, milling and grinding.
Hardox Extreme is available as standard in the following variants:
- thickness 8 – 15 mm; sheet size 2000×4000 mm
Hardox® HiAce steel is wear-resistant plate with a hardness of 450 HBW and high chemical resistance.
Hardox HiAce is resistant to corrosion found in municipal and industrial waste management, in applications such as garbage trucks, containers and parts exposed to acids in waste management facilities, recycling, landfills and biomass energy production.
The Hardox HiAce is available as standard in the following variants:
- thickness 4 – 25.4 mm; sheet size 2500 x 6000 mm
Wear-resistant Hardox® sheet for high temperatures.
Hardox® HiTemp is a highly heat-resistant wear-resistant plate for high temperatures ranging from 300 to 500 °C.
HiTemp is standardly available in these variants:
- thickness 4.7 – 51 mm; board size 2500 x 6000 mm
Strenx® 700MC D/E is a hot-rolled structural steel for cold forming with a minimum yield strength of 700 MPa. This material is usually used in components and parts in demanding load-bearing structures.
The Strenx 700 MC is available as standard in the following variants:
- thickness 2 – 10 mm; sheet size 1500 x 3000 mm
Strenx® 700 E/F is a high-strength sheet with a minimum yield strength depending on the thickness and varying between 650 and 700 MPa.
The Strenx 700 E/F is available as standard in the following variants:
- thickness 4 – 160 mm; sheet size 2500×6000 mm
Duroxite® 100 material is produced by welding abrasive-resistant materials with a high chromium content to low-carbon steel sheet using a traditional electric arc. Carbide plates are suitable for applications displayed to intensive abrasive wear in combination with moderate impacts. The multi-layer weld layers also retain full wear resistance up to 350°C and a typical surface hardness of 55 HRC even at higher temperatures up to 540°C. The material Duroxite® 100 is available in one or more weld layers up to a weld thickness of 20 mm.
Typical applications
Duroxite® 100 material is widely used in the mining industry, energy, cement industry, steel production, waste processing, glass and paper industry.
Duroxite 100 is available as standard in the following variants:
- sheet thickness 6 mm + weld thickness 4 mm; dimension 1400 x 3000 mm
- sheet thickness 10 mm + weld thickness 10 mm; dimension 1400 x 3000 mm
- the possibility of other variants
ARMOX is a high-strength, low-alloy structural steel that has been processed to provide high resistance to projectile penetration and blast protection. Steel properties are achieved by quenching and tempering to achieve the desired balance between hardness and toughness.
ARMOX is available as standard in a thickness of 3 – 100 mm; sheet size 2500 x 6000 mm.